Good Stability Aluminum Cerium Alloy AlCe Master Alloy For Aluminum Alloy Refiner
aluminum master alloy
,magnesium master alloy
Aluminum Cerium Alloy AlCe Master Alloy For An Aluminum Alloy Refiner
Name: Aluminum Cerium Alloy Molecular formula: AlCe
Size: according to user's requirements Ce content: 10%, 20%, 30%(wt)
Description: The preparation of aluminum cerium master alloy by thermal reduction method is a kind of aluminum cerium master alloy which is obtained by adding ceria and alkali metal chloride under the melting of pure aluminum. The modification duration is longer and has better remelting stability than that of sodium salt modifier, which overcomes the shortcomings of current modifier.
Specification:
| Name | AlCe-10Ce | AlCe-20Ce | AlCe-30Ce | ||||
| Molecular formula | AlCe | AlCe | AlCe | ||||
| RE | wt% | 10±2 | 20±2 | 30±2 | |||
| Ce/RE | wt% | ≥99.5 | ≥99.5 | ≥99.5 | |||
| Si | wt% | <0.1 | <0.1 | <0.1 | |||
| Fe | wt% | <0.15 | <0.15 | <0.15 | |||
| Ni | wt% | <0.05 | <0.05 | <0.05 | |||
| W | wt% | <0.01 | <0.01 | <0.01 | |||
| Cu | wt% | <0.01 | <0.01 | <0.01 | |||
| Al | wt% | The rest | The rest | The rest | |||
| property | As-cast alloy, block or plate, silver gray | ||||||
| Application | Refine aluminum alloy grains and improve the remelting stability of aluminum alloy | ||||||
| package | Conventional packaging, flexible packaging according to customer needs | ||||||
Package: Conventional packaging, 50kg per bag in iron drum packaging, also provide small package: 100g, 500g, 1kg, 5kg and other small packaging.
Used: It can fill the surface defects of aluminum alloy phase, hinder the growth of grains, refine grains and purify impurities, refine aluminum alloy grains and improve the remelting stability of aluminum alloy.
-
High Purity 99.999% Lanthanum Oxide La2O3 CAS 1312-81-8 For Ceramic Capacitor
High Purity 99.999% Lanthanum Oxide La2O3 CAS 1312-81-8 For Ceramic Capacitor Name: Lanthanum oxide CAS: 1312-81-8 Molecular formula: La2O3 Molecular weight: 325.81 Description: The rare earth chloride solution after cerium removal uses the neutral phosphine extractant dimethylheptyl methylphosphonate (P350), and the P350-kerosene system is used for 35 to 38 levels of extraction to separate lanthanum from other rare earths. The solution was neutralized with ammonia water,
-
Cerium(IV) Hydroxide Ce(OH)4 CAS 12014-56-1 For Exhaust Gas Purification Catalyst
Cerium(IV) Hydroxide Ce(OH)4 CAS 12014-56-1 For Exhaust Gas Purification Catalyst Name: Cerium(IV) hydroxide Molecular formula: Ce(OH)4 CAS: 12014-56-1 Molecular weight: 208.15 Description: Cerium hydroxide is light yellow or brownish yellow powder, insoluble in water and weak acid, soluble in concentrated acid, and generates corresponding salt. Absorbing carbon dioxide in the air to produce cerium carbonate. The mixed light rare earth ores were roasted by sodium carbonate
-
Lanthanum Chloride Hydrate LaCl3 7H2O CAS 10025-84-0 For Sewage Treatment
Lanthanum Chloride Hydrate LaCl3 7H2O CAS 10025-84-0 For Sewage Treatment Name: Lanthanum chloride hydrate Molecular formula: LaCl3.7H2O CAS: 10025-84-0 Molecular weight: 371.37 Description: Lanthanum Chloride is soluble in water and acid, slightly soluble in ethanol. A proper amount of lanthanum oxide is dissolved in an excess of 2mol / L HCl, further concentrated after a few hours of heating reaction, and the precipitated crystal is lanthanum chloride hydrate after a few
-
DyH3 Dysprosium Hydride CAS 13537-09-2 For Permanent Magnet Additives
Dysprosium Hydride DyH3 CAS 13537-09-2 For Additives Of Permanent Magnet Name: Dysprosium hydride, Dysprosium trihydride Molecular formula: DyH3 CAS: 13537-09-2 Molecular weight: 165.52 Description: Dysprosium hydride is gray-black or brownpowder, Dysprosium metal is introduced into hydrogen to absorb hydrogen to obtain brittle dysprosium hydride solid. Specification: NameDyH3_3NDyH3_2NMolecular formulaDyH3DyH3CAS13537-09-213537-09-2Total rare earth TREM%≥99.0≥99.0Dy/TREM%≥99
Please Use Our Online Inquiry Contact Form Below If You Have Any Questions, Our Team Will Get Back To You As Soon As Possible