1.4-1.8um Rare Earth Polishing Powder , Crystal Agate Gem Polishing Powder
cerium oxide polishing powder
,ceo2 powder
Rare Earth Polishing Powder KP1003 1.4-1.8um For Polishing Of Crystal, Gem and Agate
Name: Rare earth polishing powder, cerium oxide polishing powder Type: KP1003
D50: 1.4-1.8um TREO: ≥90%
Description: The main component of rare earth polishing powder is CeO2. According to the amount of CeO2, cerium polishing powder can be divided into two categories: one is the high-quality and high-quality cerium polishing powder with high CeO2 content, generally CeO2 / TREO ≥ 80%; the other is the low-cost low-ce polishing powder with low CeO2 content, whose cerium content is about 50%, or less than 50%. The rest is composed of La2O3, Nd2O3 and Pr6O11. As for ceria polishing powder, the higher the grade of ceria is, the greater the polishing ability is, and the longer the service life is. Especially when the hard glass is circularly polished for a long time (quartz, optical lens, etc.), it is better to use high-grade ceria polishing powder.
Specification:
| Physical and chemical properties | KP1003 | |
| Chemical composition | Total rare earth TREO % | ≥90 |
| CeO2/TREO % | ≥60 | |
| F % | ≤5 | |
| LOI % | ≤2 | |
| Physical performance index | D50 um | 1.4-1.8 |
| D90 um | ≤9.0 | |
| pH | 6-8 | |
| Color | White or Off-white | |
| package | Carton packing, 20kg / carton | |
| Application area | Polishing of common optical glass, lens, crystal, gem, agate and all kinds of prism and spectacle abrasives, etc | |
Packing: 20kg carton packaged, also provided small package: 1kg, 5kg and so on.
Uses: Mainly used for polishing of common optical glass, lens, crystal, gem, agate and all kinds of prism and spectacle abrasives, etc.
-
High Purity 99.999% Lanthanum Oxide La2O3 CAS 1312-81-8 For Ceramic Capacitor
High Purity 99.999% Lanthanum Oxide La2O3 CAS 1312-81-8 For Ceramic Capacitor Name: Lanthanum oxide CAS: 1312-81-8 Molecular formula: La2O3 Molecular weight: 325.81 Description: The rare earth chloride solution after cerium removal uses the neutral phosphine extractant dimethylheptyl methylphosphonate (P350), and the P350-kerosene system is used for 35 to 38 levels of extraction to separate lanthanum from other rare earths. The solution was neutralized with ammonia water,
-
Cerium(IV) Hydroxide Ce(OH)4 CAS 12014-56-1 For Exhaust Gas Purification Catalyst
Cerium(IV) Hydroxide Ce(OH)4 CAS 12014-56-1 For Exhaust Gas Purification Catalyst Name: Cerium(IV) hydroxide Molecular formula: Ce(OH)4 CAS: 12014-56-1 Molecular weight: 208.15 Description: Cerium hydroxide is light yellow or brownish yellow powder, insoluble in water and weak acid, soluble in concentrated acid, and generates corresponding salt. Absorbing carbon dioxide in the air to produce cerium carbonate. The mixed light rare earth ores were roasted by sodium carbonate
-
Lanthanum Chloride Hydrate LaCl3 7H2O CAS 10025-84-0 For Sewage Treatment
Lanthanum Chloride Hydrate LaCl3 7H2O CAS 10025-84-0 For Sewage Treatment Name: Lanthanum chloride hydrate Molecular formula: LaCl3.7H2O CAS: 10025-84-0 Molecular weight: 371.37 Description: Lanthanum Chloride is soluble in water and acid, slightly soluble in ethanol. A proper amount of lanthanum oxide is dissolved in an excess of 2mol / L HCl, further concentrated after a few hours of heating reaction, and the precipitated crystal is lanthanum chloride hydrate after a few
-
DyH3 Dysprosium Hydride CAS 13537-09-2 For Permanent Magnet Additives
Dysprosium Hydride DyH3 CAS 13537-09-2 For Additives Of Permanent Magnet Name: Dysprosium hydride, Dysprosium trihydride Molecular formula: DyH3 CAS: 13537-09-2 Molecular weight: 165.52 Description: Dysprosium hydride is gray-black or brownpowder, Dysprosium metal is introduced into hydrogen to absorb hydrogen to obtain brittle dysprosium hydride solid. Specification: NameDyH3_3NDyH3_2NMolecular formulaDyH3DyH3CAS13537-09-213537-09-2Total rare earth TREM%≥99.0≥99.0Dy/TREM%≥99
Please Use Our Online Inquiry Contact Form Below If You Have Any Questions, Our Team Will Get Back To You As Soon As Possible